By: Dr. Thomas Read
Tel: (707) 544-2374
Email Dr. Read
The annealed borosilicate glass pie plate failed as a result of “thermal shock”. There were multiple origins for the failure, and these all initiated at damage sites on the bottom of the Pyrex baking dish. It appears that the bottom of the pie plate was convex. Thus, setting the dish down and moving it on hard (abrasive) surfaces such as tile or granite counters created bottom “rim” damage. When the hot dish was placed on a cold surface, tensile stresses were created on the bottom of the dish where the cold surface was contacted, and these caused the failure to initiate at the scratch damage sites.
Figure #1: Photograph of the top side of the failed Pyrex dish after re-assembly. The failure had multiple origins, and these were all on the bottom of the dish. The origins were scratches created by setting and moving the Pyrex dish on a hard counter surface such as tile or granite. Setting the hot dish on a cold surface created tensile stresses on the bottom of the dish. These stresses created cracks from the scratch damage; these grew and generated the failure. The arrows on the dish show the travel directions of the various cracks.
Figure #2: Photograph of the rim of damage on the convex bottom of the dish. Sliding and rotating the dish on hard (abrasive) surfaces created the damage sites that became the origins of the failure.
Figure #3: Photograph of a representative origin on the Pyrex baking dish bottom. The multiple cracks were caused by thermal stresses created when the hot pie plate was put on a cold surface.
Dr. Thomas L. Read, CEO of Read Consulting received his PhD. from Stanford University in 1972. He has over 25 years of manufacturing experience in electronics, metallurgy, factory safety, failure analysis, glass fracture, glass failure and bottle failure. As a member of the electronics industry, Dr. Read has earned process patents and has an extensive background in manufacturing techniques. In parallel, he has spent over twenty five years as a consultant to attorneys and engineers in the areas of failure analysis, metallurgy, glass fracture, glass failure, bottle failure, factory safety, manufacturing problems, intellectual property and patent disputes.
©Copyright - All Rights Reserved
DO NOT REPRODUCE WITHOUT WRITTEN PERMISSION BY AUTHOR.
11/8/2011· Failure Analysis
Root Cause Failure Analysis of Tempered Glass Door
By: Dr. Thomas Read
Glass Failure Analysis Expert Witness performs a failure analysis of a several tempered glass doors that had "spontaneously" failed at a construction site. The objective of this glass failure analysis is to determine the cause of failure and make recommendations to the contractor.
4/5/2024· Failure Analysis
Defending Assets: A Legal Perspective On Corrosion Prevention
Corrosion poses a significant threat to various industries, and its impact on assets cannot be underestimated. As an engineer, you might wonder how this topic can be of interest to an attorney. Well, attorneys play a crucial role in protecting their clients' interests, and corrosion prevention aligns seamlessly with legal strategies aimed at safeguarding assets. In this article, we will explore the legal implications of corrosion and the role attorneys can play in mitigating its risks.
5/17/2011· Failure Analysis
Plumbing Failure Analysis: Stress Corrosion Cracking of Yellow Brass
By: Dr. Thomas Read
A plumbing failure analysis was performed to determine why a cold water supply line to a bathroom sink had failed after only one year of service.